Question

In: Mechanical Engineering

Consider a single crystal of a cubic metal that is subjected to a tensile stress along...

Consider a single crystal of a cubic metal that is subjected to a tensile stress along the [0 1 2 ] direction.

Calculate the Schmidt factor for the following slip systems. In each case sketch the tensile axis as well as the slip plane and slip direction.

a) (0 -1 1) [0 1 1]

b) (1 0 1) [-1 -1 1]

c) (0 1 0) [ -1 0 1 ]

d) If the crystal above is subjected to an increasing applied stress, which of the systems above will undergo slip first. Explain your answer.

e) What is the value of the ratio t CRSS / (sigma)y at the point of slipping?

Solutions

Expert Solution


Related Solutions

A single crystal of a metal is oriented for a tensile test such that its slip...
A single crystal of a metal is oriented for a tensile test such that its slip plane normal makes an angle of 64.2° with the tensile axis. Three possible slip directions make angles of 30°, 48°, and 78° with the same tensile axis. (a) Which of these three slip directions is most favored? (b) If plastic deformation begins at a tensile stress of 1.6 MPa (232.1 psi), determine the critical resolved shear stress for this metal
Consider a cubic I crystal with a lattice parameter of 3 Å, and a single atom...
Consider a cubic I crystal with a lattice parameter of 3 Å, and a single atom at each lattice point.  Calculate the structure factor (F) and its square magnitude |?|2 for the primitive and conventional unit cells. Indicate for each the constraints on ℎ+?+? for systematic absences (|?|2=0).
A single crystal of a metal that has the FCC crystal structure is oriented such that...
A single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [110] direction. The critical resolved shear stress for this material is 1.75 MPa. 1) Calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the (1-10) direction. 2) Calculate the magnitude of applied stress necessary to cause slip to occur on the (111) plane in the (10-1)direction. 3) Which...
A cubic metal (radius of hypothetical touching atomic spheres:r=0.77Å) showsplastic deformation by slip along...
A cubic metal (radius of hypothetical touching atomic spheres: r=0.77Å) showsplastic deformation by slip along the<111>directions. Based on thisinformation, deduce the planar packing density (atoms/m2) for its densest familyof planes.
(c) Draw a schematic graph of resolved shear stress versus shear strain for a single crystal...
(c) Draw a schematic graph of resolved shear stress versus shear strain for a single crystal of a pure metal. Clearly label the point of the critical resolved shear stress and the three subsequent stages of dislocation behaviour. Describe these three stages. (d) Explain why the critical resolved shear stress is much lower than the theoretical strength, based on the force required to break atomic bonds within the structure.
Consider a metal with an FCC crystal structure. The interplanar spacing is known to be (2.0000x10^-1)...
Consider a metal with an FCC crystal structure. The interplanar spacing is known to be (2.0000x10^-1) nm. If the first-order angle of diffraction (2*theta) is found to be (4.50x10^1) ° for the (311) set of planes in this metal, what wavelength of monochromatic x-radiation (in nm) must have been used for the diffraction? Use scientific notation with 3 significant figures (X.YZ x 10^n). Note that Avenue automatically enters x10, so you only need to enter X.YZ and n.
For the given plane of a cubic crystal structure, find the followings
For the given plane of a cubic crystal structure, find the followings 1. Miller indices 2. Type of a cubic crystal structure 3. Relation of lattice parameter "a" and the radius "r" 4. If the radius of the atom is "6 nm", find the planar density in atoms/nm 5. In your opinion, is it the densest plane of this cubic crystal structure? In case otherwise draw the densest plane of this cubic crystal structure and compare its planar density in atoms/nm2.
Biomaterials question: Biomedical Engineering Would a perfect single-crystal metal (i.e. no defects) be able to deform...
Biomaterials question: Biomedical Engineering Would a perfect single-crystal metal (i.e. no defects) be able to deform plastically? Please explain using your knowledge of crystal structure, point, line, and plane defects.   
- Calculate the atomic packing factor for Face Centered cubic and Body Centered Cubic crystal structures
- Calculate the atomic packing factor for Face Centered cubic and Body Centered Cubic crystal structures
The results of a tensile experiment on a metal is given in the table below. The...
The results of a tensile experiment on a metal is given in the table below. The tensile sample had circular cross section with the diameter of 10 mm and initial gauge length of 60 mm. Use this table and calculate: Force (N) Measured Length (mm) Region 0 60 Elastic 15708 60.15 Elastic 31416 60.3 Elastic 35343 60.6 Plastic 36128 61.2 Plastic 36914 63 Plastic 37306 66 Plastic (a) The Young modulus of this metal (in GPa) (b) The modulus of...