Question

In: Civil Engineering

Results obtained from a tension test on a bar of uniform cross section 10 mm x...

Results obtained from a tension test on a bar of uniform cross section 10 mm x 10 mm
subjected to an axial pull of 8000 N were tabulated. The lateral dimensions of the bar were found
to be changed to 9.9985 mm x 9.9985 mm while using a material having modulus of rigidity equal
to 0.8 x 107 N/cm2. By determining the values for different moduli, identify the properties of
material and establish the relationship between them. What changes will happen to the volume if
the length of the bar is equal to 2.5 m? Based on the results obtained discuss how the elastic
constants are related to the deformation of the bar?

Solutions

Expert Solution

Since there are some equations, I preferred a handwritten note. Results are tabulated in the answer for your easier understanding. Hope that it is clear for you and it really helped you.

If you are clear, please help me by rating it with a thumbs up.

In case of any doubt, please feel free to ask in the comment section. Thank you.


Related Solutions

Results obtained from a tension test on a bar of uniform cross section 10 mm x...
Results obtained from a tension test on a bar of uniform cross section 10 mm x 10 mm subjected to an axial pull of 8000 N were tabulated. The lateral dimensions of the bar were found to be changed to 9.9985 mm x 9.9985 mm while using a material having modulus of rigidity equal to 0.8 x 107 N/cm2. By determining the values for different moduli, identify the properties of material and establish the relationship between them. What changes will...
Results obtained from a tension test on a bar of uniform cross section 10 mm x...
Results obtained from a tension test on a bar of uniform cross section 10 mm x 10 mm subjected to an axial pull of 8000 N were tabulated. The lateral dimensions of the bar were found to be changed to 9.9985 mm x 9.9985 mm while using a material having modulus of rigidity equal to 0.8 x 107 N/cm2. By determining the values for different moduli, identify the properties of material and establish the relationship between them. What changes will...
Results obtained from a tension test on a bar of uniform cross section 10 mm x...
Results obtained from a tension test on a bar of uniform cross section 10 mm x 10 mm subjected to an axial pull of 8000 N were tabulated. The lateral dimensions of the bar were found to be changed to 9.9985 mm x 9.9985 mm while using a material having modulus of rigidity equal to 0.8 x 107 N/cm2. By determining the values for different moduli, identify the properties of material and establish the relationship between them. What changes will...
2: Results obtained from a tension test on a bar of uniform cross section 10 mm...
2: Results obtained from a tension test on a bar of uniform cross section 10 mm x 10 mm subjected to an axial pull of 8000 N were tabulated. The lateral dimensions of the bar were found to be changed to 9.9985 mm x 9.9985 mm while using a material having modulus of rigidity equal to 0.8 x 107 N/cm2. By determining the values for different moduli, identify the properties of material and establish the relationship between them. What changes...
A bar with an equilateral triangle cross section experienced a strain of 6.5983 x 10-4 due...
A bar with an equilateral triangle cross section experienced a strain of 6.5983 x 10-4 due to an axial load of 2 kN. The dimensions of the cross section is 5 mm and the length is 300 mm. Assume that the poisson’s ratio is 0.28. What is the value of the modulus of elasticity in GPa? Ans = 280 GPa What is the value of the modulus of rigidity in GPa? Ans = 109.38 GPa What is the bulk modulus...
Consider an electron beam of uniform circular cross-section with a diameter of 1 mm. The electrons...
Consider an electron beam of uniform circular cross-section with a diameter of 1 mm. The electrons are accelerated from the cathode to the anode, which are separated by 1 m. The electrons are generated at the cathode and therefore have negligible velocity at this position. The electrons accelerate at a rate of 108 ?/?2 between the cathode and anode. The current density at the anode is 104 ?/?2 . Find the current density as a function of position between the...
A bar of n-type Si with a cross-sectional area of 1 mm x 1 mm and...
A bar of n-type Si with a cross-sectional area of 1 mm x 1 mm and a length of 1 cm is connected to a 2 V battery and is carrying a current of 2 mA at 300 K. (a) Calculate the thermal equilibrium electron and hole concentrations in the bar. (b) Calculate the dopant concentration assuming that only donors with energy level 0.148 eV away from the conduction band are present. (c) Determine the temperature at which the bar...
A 2.8 mm -diameter copper wire carries a 31 Acurrent (uniform across its cross section). A)...
A 2.8 mm -diameter copper wire carries a 31 Acurrent (uniform across its cross section). A) Determine the magnetic field at the surface of the wire. B) Determine the magnetic field inside the wire, 0.50 mm below the surface. C) Determine the magnetic field outside the wire 2.5 mm from the surface.
10 cm of copper with square cross section of 1x1 cm exposed to 200 KN tension...
10 cm of copper with square cross section of 1x1 cm exposed to 200 KN tension force caused 15% permanent reduction in cross section area , if the fracture got on this point, calculate the following: 1 – the ductility 2 – stress 3 – true stress 4- fracture stress
Lab Procedure The cross-section dimensions of the 6061-T6 aluminum bar are 0.512 in x 0.248 in....
Lab Procedure The cross-section dimensions of the 6061-T6 aluminum bar are 0.512 in x 0.248 in. Attach the lead wires of the gages to the strain indicator as a quarter bridge circuit. (Note: the black and white lead wires are the common leads.) Enter the gage factor (GF=2.11) into the strain indicator. Record the specimen number (1, 2, or 3). Balance the strain indicator and note the zero readings. Load the specimen according to the table below and record the...
ADVERTISEMENT
ADVERTISEMENT
ADVERTISEMENT